Title: Extraction of wood hemicelluloses through NaOH leaching
Other Titles: Remoção de hemiceluloses da madeira por tratamento de lixiviação alcalina com NaOH
???metadata.dc.creator???: Longue Júnior, Dalton
Colodette, Jorge Luiz
Gomes, Valéria Juste
Keywords: Lixiviação alcalina
Remoção de hemiceluloses
Xilanas
Rendimento
Alkaline leaching
Yield
Xylans
Hemicellulose extraction
Publisher: UFLA - Universidade Federal de Lavras
???metadata.dc.date???: 1-Dec-2010
Citation: LONGUE JUNIOR, D.; COLODETTE, J. L.; GOMES, V. J. Extraction of wood hemicelluloses through NaOH leaching. Cerne, Lavras, v. 16, n. 4, p. 423-429, 2010.
???metadata.dc.description.resumo???: Neste estudo, objetivou-se avaliar o impacto da remoção de hemiceluloses da madeira de eucalipto, por tratamento de lixiviação alcalina (NaOH) de cavacos, no comportamento do processo kraft (com variação da sulfidez) subsequente e na qualidade da polpa. Na lixiviação alcalina, os cavacos foram inicialmente saturados com água e posteriormente tratados com solução de NaOH, numa relação licor:madeira de 6:1 m3/t. Foram avaliados os tempos de reação de 3, 8, 14 e 18 horas, as temperaturas de 70, 84 e 90ºC e as concentrações de NaOH de 60, 80, 90, 120 e 156g/L sob condições atmosféricas. Para os tratamentos pressurizados (300 kPa), foram investigados os tempos de reação de 30, 60 e 120 minutos, a temperatura de 100ºC e as concentrações de 100, 150 e 200g/L de NaOH. A condição ótima de lixiviação alcalina foi determinada, considerando-se os teores de hemiceluloses remanescentes nos cavacos e o rendimento gravimétrico. Cavacos não submetidos ao tratamento alcalino (referência) e lixiviados com NaOH, em condições ótimas, foram cozidos pelo processo kraft até número kappa 17 – 18. Os resultados indicaram que a lixiviação alcalina dos cavacos é ineficiente na remoção das hemiceluloses da madeira estudada. A máxima remoção do acetato de 4-O-metil-glicuronoxilana foi de 42% em condições muito severas (100ºC, 60 minutos, 200g/L NaOH e 300 kPa de pressão). O rendimento do cozimento kraft dos cavacos lixiviados foi cerca de 7% inferior ao da referência.
Abstract: The aim of this work was to assess the impact of hemicellulose extraction in eucalyptus wood, through alkaline leaching (NaOH) of wood chips, on the subsequent kraft process (with varying sulphidity) and the quality of the pulp. The chips were initially saturated with water and treated with a NaOH solution in a liquor to wood ratio of 6:1 m3/t. The reaction times (3, 8, 14 and 16 hours), temperatures (70, 84 and 90ºC) and NaOH concentrations (60, 80, 90, 120 and 156g/L) were assessed in atmospheric conditions. In the pressurized treatments (300 kPa), the reaction times, temperature and NaOH concentrations assessed were, respectively: 30, 60 and 120 minutes, 100ºC and 100, 150 and 200g/L. The optimal alkaline leaching condition was determined taking into account the hemicellulose concentrations remaining in the chips and the gravimetrical yield. Chips not subjected to alkaline treatment (control) and leached with NaOH in optimum conditions were kraft cooked until kappa number 17 – 18. The results indicate that alkaline leaching of chips is not efficient in extracting hemicelluloses in the wood studied. The highest extraction of 4-Omethyl-glucuronoxylan acetate reached 42% in very severe conditions (100ºC, 60 minutes, 200g/L of NaOH and 300 kPa pressure). The pulp yield of the leached chips was approximately 7% lower than that of the non-leached chips (control).
Other Identifiers: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0104-77602010000400001
???metadata.dc.language???: en
Appears in Collections:CERNE

Files in This Item:

There are no files associated with this item.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.


View Statistics

 


DSpace Software Copyright © 2002-2010  Duraspace - Feedback