Título : Effect of early age curing carbonation on the mechanical properties and durability of high initial strength portland cement and lime-pozolan composites reinforced with long sisal fibres
Autor: Neves Junior, Alex
Ferreira, Saulo Rocha
Toledo Filho, Romildo Dias
Fairbairn, Eduardo de Moraes Rego
Dweck, Jo
Palavras-chave: Early age curing carbonation
Mechanical properties
Sisal fibres
Thermal analysis
Publicador: Elsevier
Data da publicação: Abr-2019
Referência: NEVES JUNIOR, A. et al. Effect of early age curing carbonation on the mechanical properties and durability of high initial strength portland cement and lime-pozolan composites reinforced with long sisal fibres. Composites Part B: Engineering, [S.l.], v. 163, p. 351-362, Apr. 2019.
Abstract: This paper presents the results of a study about the mechanical behaviour, before and after aging, of two cement-based composites reinforced with long sisal fibres cured at early age in a CO2 environment. After curing, samples of both composite systems were submitted to wetting and drying cycles to accelerate the aging of the materials allowing the evaluating of the efficiency of the CO2 treatment. Besides promoting CO2 capture, the used cure also allowed the increase in the durability of the sisal fibre-cement based composites by the Calcium Hydroxide (CH) consumption and pH decrease promoted by the carbonation reactions. The lime-pozzolanic material composite was also treated with CO2 at early stages of formation, with the carbonation and pozzolanic reactions acting simultaneously to deplete the Ca(OH)2 thus improving its durability. Four-point bending test, thermogravimetry analysis of the matrix and SEM analysis of the fibres were done before and after aging to study the durability mechanisms of the composites. The obtained results showed that the CH free cement-based composite containing metakaolin and fly ash presented the best mechanical behaviour before and after accelerated aging. The early age carbonation of the lime-pozolan composites improved its mechanical response, before and after accelerated aging, when compared with the non-carbonated samples. The thermogravimetry test showed that the increase of the carbonation time of the reference Portland cement-based composite consumed the CSH, compromising the ductility and strain capacity of this composite family after aging. The SEM pictures showed petrified fibre effect by the migration of hydrated products after 10 and 20 cycles of ageing for this composite system.
URI: https://www.sciencedirect.com/science/article/pii/S1359836818310400
http://repositorio.ufla.br/jspui/handle/1/34852
Idioma: en_US
Aparece nas coleções:DEG - Artigos publicados em periódicos

Arquivos associados a este item:
Não existem arquivos associados a este item.


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.